Title: Поведение низкоуглеродистой стали при статическом и циклическом нагружениях
Other Titles: Поведінка низьковуглецевої сталі при статичному і циклічному навантаженнях
Behavior of Low-Carbon Steel at Static and Cyclic Loadings
Authors: Вакуленко, Игорь Алексеевич
Вакуленко, Ігор Олексійович
Vakulenko, Ihor O.
Ефременко, Василий Георгиевич
Єфременко, Василь Георгійович
Efremenko, Vasylyi H.
Keywords: плотность подвижных дислокаций
твердорастворное упрочнение
размер зерна феррита
усталостная прочность
дислокационная ячейка
густина рухомих дислокацій
твердорозчинне зміцнення
розмір зерна фериту
міцність при втомі
дислокаційна комірка
density of mobile dislocations
solid solution strengthening
size of grain of ferrite
strength of fatigue
dislocation cell
КТМ
Issue Date: 2014
Publisher: ПГТУ
Abstract: RU: В статье на примере низкоуглеродистой стали проведен анализ влияния размера зерна феррита на развитие пластического течения в условиях статического и циклического нагружения. Осуществлена оценка требуемой плотности подвижных дислокаций для поддержания условий непрерывности распространения пластической деформации.
UK: У статті, на прикладі низьковуглецевої сталі проведений аналіз впливу розміру зерна фериту на розвиток пластичної течії в умовах статичного і циклічного навантаження. Здійснена оцінка необхідної густини рухомих дислокацій для підтримки умов безперервності розповсюдження пластичної деформації.
EN: In the article, on the example of low-carbon steel (0.1 % C), the analysis of influence of size of grain ferrite on development of plastic flow in the conditions of static and cyclic loading is conducted. Different modes of heat treatment and thermomechanical treatment were applied to get experimental samples. The investigation was fulfilled using optical quantities metallography as well transmission microscopy. The assessment of separate influence of solid solution state and the ferrite grain boundaries on the yield stress and the fatigue strength of the metal was carried out by analyzing the chart type of the Hall-Petch law. The estimation of required density a mobile dislocations is carried out for maintenance of terms continuity distribution plastic flow. It was found that for low-carbon steel under cyclic loading the strengthening effect of grain boundaryprostrate exceeds solid-solution strengthening at a much finer structure compared with static stretching. To maintain the continuity propagation of plastic deformation at the same size of ferrite grain under cyclic loading conditions requires about twice as much of mobile dislocations than under the unidirectional deformation.
Description: Вакуленко И. А. Поведение низкоуглеродистой стали при статическом и циклическом нагружениях / И. А. Вакуленко, В. Г. Ефременко // Вісник Приазовського державного технічного університету. Серія : Технічні науки. - 2014. - Вип. 29. - С. 64-70.
URI: http://eadnurt.diit.edu.ua/jspui/handle/123456789/4093
Appears in Collections:Статті КТМ

Files in This Item:
File Description SizeFormat 
vpdty_2014_29_10.pdf7,02 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.